The large welding current caused the formation of quenched martensite and the high residual stresses in the welding zone, resulting in the increase of zinc sensitivity of hydrogen attack.
结果表明：由于焊接电流过大，使焊缝产生淬火马氏体组织及较大的焊接残余应力，导致镀锌氢脆敏感性增加，造成吸油盘发生氢脆开裂。