The results show that the SSFs' bending strength gradually increases and the open porosity falls with increasing the slurry loading in precursor;
研究发现：随前驱体中浆料浸入量的增加，泡沫制品的抗弯强度逐渐提高，开孔率有所降低；
Correlation coefficients between the thermal conductivity and bulk density, open porosity, permeability and raw material grade was obtained respectively.
另外，还计算了导热系数与体积密度、显气孔率、透气度和原料等级之间的相关系数。
So that, it is necessary to adopt very sinterable UO2 powder and suitable pelleting and sintering conditions to minimize open porosity and small porosity.
因此，必须采用烧结性良好的UO_2粉末和合适的成型烧结条件以使开口孔隙度和细孔隙度降至最低。
The foamed ceramic material with high open porosity is characterized by low apparent density , high permeability, and resistance to high temperature and chemical corrosion.
泡沫陶瓷具有密度小、透气性高、耐高温、抗化学腐蚀等特性。
The use of U3O8 additive can improve the pellet microstructure, but result in decrease of pellet density and increase of open porosity, which contributes strongly to moisture.
采用U_3O_8添加剂可改善芯块微观结构，但同时使芯块密度下降，开口孔隙度增加进而导致吸湿加剧。
The effects of sintering schedule on the shrinkage, open porosity and bending strength of the stainless steel foam with 3-D opened network structure were investigated in this paper.
研究了烧结制度对具有三维通孔网状结构泡沫不锈钢的线收缩率、开孔孔隙度、抗弯强度的影响。
The compactness bending strength, compressive strength, shore-hardness of carbon slides impregnated with metals were increased; while open porosity and electrical resistivity decreased.
炭滑板经浸渍金属后，致密性、抗折强度、抗压强度、肖氏硬度明显提高，而开口气孔和电阻率降低。
Based on the experiment results on three kinds of open graded ATPB, it is concluded that asphalt content should be above 2.5% and porosity should be above 18%.
本文经对三种开级配的沥青稳定碎石进行了试验研究，得出ATPB的沥青用量应在2.5%以上，空隙率在18%以上的结论。
The porosity of porous Al-Si alloy is 40~80% and percentage of open-cell is above 85%, bom of which vary with the fabrication process of preform.
孔隙率在40～80%，孔隙连通率在85%以上，孔隙的大小和孔隙率取决于预制块的制备工艺。
The porosity of porous Al-Si alloy is 40~80% and percentage of open-cell is above 85%, bom of which vary with the fabrication process of preform.
孔隙率在40～80%，孔隙连通率在85%以上，孔隙的大小和孔隙率取决于预制块的制备工艺。