• Results indicate that the fatigue strength of welded joints is lower than that of the parent metal.

    结果表明焊接接头高疲劳性能低于疲劳性能。

    youdao

  • The Bucky adhesive tape take the polyethylene and the gauze textile fiber heat compound as a parent metal.

    胶带聚乙烯纱布纤维复合基材。

    youdao

  • The tensile strength and the elongation percentage of the parent metal and the weld zone increased slightly.

    冲击处理使焊缝区材区的强度伸长率均有所增加。

    youdao

  • Metallurgical tests of cross-sectional weld samples indicate a minimal heat-affected zone that is identical to the parent metal.

    样品金相检验表明,成品的最小热影响与母体金属完全相同。

    youdao

  • This paper describes in detail principles for appropriete selection of steel, compatibility of parent metal with welding material, etc.

    结合武钢三炼钢厂房工程建设需要,本文详细阐述钢材选用原则,新钢种焊接材料的匹配问题;

    youdao

  • Intense and manifold plastic deformation occurs in parent metal near interface zone, and deformation mostly fastens on eddy in front of wave.

    界面基体金属发生剧烈多种形式塑性变形,变形主要集中于波漩涡附近。

    youdao

  • This zone is traditionally called shear zone in view of fact that the material in the final form would be removed by shear from the parent metal.

    考虑最终形状中的材料通过剪切母体金属去除区域传统上称为剪切

    youdao

  • Sliver. An extremely thin elongated piece of metal that has been rolled into the surface of the parent metal to which it is attached - usually by only one end.

    重皮。扎基体金属表面通常只有一端基体金属相连的金属长条

    youdao

  • Where filler materials having tensile properties deviating (downwards) from the parent metal are used, this fact must be taken into account when dimensioning the weld joints.

    部分开始使用具有伸缩性的填角材料之处,计算焊缝应该考虑这种情况

    youdao

  • According to the electrochemical impedance spectroscopy results, the corrosion products plating on alloys surface are partly protective to the parent metal with immersion time.

    阻抗测试结果显示,随着浸泡时间延长,腐蚀产物合金表面沉积,基体金属具有一定的保护作用

    youdao

  • The mechanical testing results showed that tensile strengths of samples welded by direct welding is only 31.24% of that of the parent metal, and 50.89% of that by "in-situ" welding.

    力学性能试验结果表明,不加填充材料焊接时,试样拉伸强度强度31.24%;进行原位焊接时,试样强度达到母材强度的50.89%。

    youdao

  • This adhesive tape take imports the white beautiful patterned paper as a parent metal, one-sided spreads the cloth weathering resistance rubber is presses the sensitive rubber to become.

    胶带进口白色基材单面涂布耐候性橡胶而成。

    youdao

  • The tensile test fracture area locates on weld seam, and the hardness near HAZ fusion line is the highest, away from the fusion line, the hardness declines and reach the parent metal hardness.

    焊接接头拉伸试验断裂部位焊缝。焊接HAZ熔合线附近硬度最高远离熔合线硬度降低逐渐接近金属的硬度。

    youdao

  • The results show the accumulated damage of reformer tubes is localized, and the damage of the weldment located at the lower part of reformer tubes is more serious than that of the parent metal.

    结果表明累积损伤具有局部性下部高温段的焊缝损伤严重

    youdao

  • The welding metal can form granular bainite structure and mechanics property of welding joints is consistent with the parent metal. The result shows that this welding electrode can meet the need.

    通过分析焊接接头组织力学性能表明辙叉性能基本一致能够满足使用要求。

    youdao

  • Gaseous NF3 containing 0.1% or less active fluorides (calculated as HF) was found to be noncorrosive toward several different parent and welded metal specimens.

    含有0.1%更少活泼氟化物(认为HF)的气态NF 3发现对于几种不同焊接金属试验品是没有腐蚀性的。

    youdao

  • The results showed that the principal factors affecting the metal background contents were landforms for plain area and soil parent material for mountain area.

    分析结果表明影响土壤元素背景主要因素平原地区地貌条件,山区是成土母质

    youdao

  • The results showed that the principal factors affecting the metal background contents were landforms for plain area and soil parent material for mountain area.

    分析结果表明影响土壤元素背景主要因素平原地区地貌条件,山区是成土母质

    youdao

$firstVoiceSent
- 来自原声例句
小调查
请问您想要如何调整此模块?

感谢您的反馈,我们会尽快进行适当修改!
进来说说原因吧 确定
小调查
请问您想要如何调整此模块?

感谢您的反馈,我们会尽快进行适当修改!
进来说说原因吧 确定