Large thick-section ductile Iron housing easily produces casting defects such as shrinkage cavity, shrinkage porosity, graphite floating and spheroidizing decay.
大型厚断面球墨铸铁件在铸造过程中极易产生缩孔、缩松、石墨漂浮及球化衰退等铸造缺陷。
It is discussed that adiabatic material, as well as ratio of height and width effected solidification, shrinkage cavity and shrinkage porosity.
讨论了锭模的高宽比、绝热板材质对凝固位置及缩孔疏松的影响。
The influence of chemical composition, inoculation process, temperature of molten iron and pouring system on the formation of shrinkage cavity and porosity was described.
叙述化学成分、孕育工艺、铁液温度及浇注系统等因素对薄壁球铁铸件缩孔和缩松形成的影响。