  The results show that during the solution treatment of Mg-8%Al-2%Ga alloy,the secondary β-Mg17Al12 phases dissolve at first,and then the divorced eutectic β-Mg17Al12 phases. With the solution time increasing,the grains are growing up gradually.

  结果表明,Mg-8%Al-2%Ga合金固溶处理时,首先固溶的是片状的次生β-Mg17Al12相,然后是离异共晶β-Mg17Al12相;随着固溶时间的延长,晶粒逐渐长大,并且在随后的时效处理时析出方式由非连续析出为主逐渐变为连续析出为主。