In this paper, we raise really available measures through the investigation, analysis, test and research about the stress corrosion cracking of pressure vessel for ammonia refrigerating equipments.
通过对氨制冷压力容器应力腐蚀开裂进行调查、分析、试验和研究,提出切实可行的对策措施。
The stress corrosion cracking(SCC) of carbon steels in aqueous alkali was studied by electrochemical technique, stress corrosion test under constant load and repassivation test.
本工作通过电化学,恒载荷应力腐蚀和再钝化试验,对碳钢在碱溶液中的应力腐蚀破裂进行了研究。
Stress corrosion cracking of an X60 pipeline steel in soil containing water has been investigated using slow strain rate test.
用光滑试样慢应变速率拉伸法研究了X60管线钢在含水土壤中的应力腐蚀。
By stepwise regression analysis of test results, the notabilities of effect on stress corrosion cracking susceptive indexes of medium parameters are revealed.
通过试验数据的逐步回归分析,进一步揭示试验介质参数对应力腐蚀敏感性指数影响的显著性。
The stress corrosion cracking(SCC)behavior of X70 steel welded joint was investigated in a near-neutral pH solution by fluctuant slow strain rate test(F-SSRT).
分析温度、应力(应变)和慢应变率等因素对极化曲线的影响,并讨论温度、应力和慢应变率对管道钢发生应力腐蚀开裂的驱动作用。
The stress corrosion cracking(SCC)behavior of X70 steel welded joint was investigated in a near-neutral pH solution by fluctuant slow strain rate test(F-SSRT).
分析温度、应力(应变)和慢应变率等因素对极化曲线的影响,并讨论温度、应力和慢应变率对管道钢发生应力腐蚀开裂的驱动作用。