The results showed that fly-ash mortar could be used to replace normal morter and they also provided the basis in theory for...
结果表明，粉煤灰砌筑干粉能够替代普通水泥砂浆，为粉煤灰砌筑干粉推广应用提供了理论依据。
The results showed that fly-ash mortar could be used to replace normal morter and they also provided the basis in theory for further popularizing and applying fly-ash mortar.
结果表明，粉煤灰砌筑干粉能够替代普通水泥砂浆，为粉煤灰砌筑干粉推广应用提供了理论依据。
The reasonable mix of fly ash cement mortar and fly ash lime cement mortar is put forth.
并在试验基础上，提出了较为合理的掺粉煤灰的水泥砂浆、石灰水泥砂浆的配比。
Experimental results indicate the following: firstly, the initial cracking time of mortar increase and free shrinkage decrease with the percentage of blended fly ash increasing.
试验表明，随着粉煤灰掺量的增加，粉煤灰砂浆的初始开裂时间显著增加。
The fly ash series dry mixing mortar powder has been developed by using low quality of fly ash.
利用低品质粉煤灰研制出粉煤灰系列干拌砂浆粉。
This paper presents basic mechanics properties about building mortar admixed with fly ash "two ashes powder".
本文介绍了使用粉煤灰双灰粉的建筑砂浆的性能。
On the paper, constrative experiment of fly ash cement mortar, fly ash line cement mortar and datum cement mortar has been done. The influence of mortar's performance fly ash made is analysised.
本文通过对掺入粉煤灰的高强水泥砂浆、高强石灰水泥砂浆与基准砂浆的对比试验，分析了粉煤灰对砂浆性能的影响。
The influence of different contents of slag, fly ash and zeolite powers on the strength of alite-calcium barium sulphoaluminate cement mortar is investigated, and the reaction mechanism is discussed.
研究不同掺量的矿渣、粉煤灰和沸石粉对阿利特-硫铝酸钡钙水泥砂浆强度的影响规律，并对其反应机理进行探讨。
The test results indicated that the bond splitting tensile strength of modified fly ash mortar was best in joint materials of sorts.
试验结果表明，各种接缝面材料中，粉煤灰改性砂浆的劈裂抗拉强度最大，效果最好。
This paper deals with the proportion design, main properties, practical applications and economic benefit of building mortar admixed with adding Calcium fly ash.
本文介绍了用增钙粉煤灰配制建筑砂浆的配比试验，增钙粉煤灰砂浆的基本性能、工程应用及经济效益。
This Fly Ash is used as cement mortar, concrete mixture and concrete reducing water agent.
本文就其用于配制砌筑水泥，作混凝土掺和料和混凝土减水剂进行介绍。
The thermal insulating masonry mortar is made of fly ash, ordinary Portland cement and light aggregate as main raw materials, added with every admixture.
保温砌筑砂浆是以粉煤灰、普通硅酸盐水泥、轻骨料为主要材料，配以各种外加剂而制成。
The effects of fly ash, water retention agent, re-dispersible latex powder and water reducing agent on performance of mortar were.
研究了粉煤灰、保水剂、可再分散乳胶粉、减水剂等对砂浆性能的影响，并探讨各种外加剂对砂浆的改性机理。
The effect of mineral blenders includes ground steel slag and fly ash on the electrical conductivity of cement mortar was studied.
试验研究了掺加磨细钢渣、粉煤灰等掺合料后水泥浆体导电性能的变化。
Entraining fly ash and mineral powder with high quality can increase the initial fluidity of cement mortar and the fluidity retention capacity.
掺加较优质的粉煤灰和矿粉有利于提高砂浆的初始流动性和流动性保持能力。
The amount of fly ash addition has an important influence on properties and economical benefit of the mortar.
粉煤灰掺量多少对砂浆的技术性能与经济效益具有重要影响。
As the stone waste powder had less the active ingredient, Using the stone waste powder to replace small or all of fly ash would reduce the later strength of the mortar.
由于废石粉中活性成分较少，所以用废石粉部分或全部取代粉煤灰时，会使砂浆后期强度降低。
In this paper, we mainly study the influence of the cement mortar performance caused by the separating fly ash and the size reduction fly ash, besides, we also study the different fly ash's figure.
本文研究了比表面积相近的由分选粗灰粉磨而成的磨细粉煤灰与分选细粉煤灰的颗粒形貌及水泥胶砂性能。
A new type of brick, with a uniform height achieved by covering it with fly-ash slurry mortar, has also been developed.
一种具有统一高度的、用粉煤灰浆制作的新型砖也已经被开发出来。
The compression tests are made on 18 autoclaved fly ash perforated brick masonry samples and 15 common clay brick masonry samples taking mortar strength as main parameter.
以砂浆强度为主要参数，对18个蒸压粉煤灰多孔砖砌体试件及15个普通黏土砖砌体试件进行受压试验。
This paper concentrates on the influence of the mixture of fly ash and slag powder on cement mortar strength and resistance to simulating acid rain.
研究了粉煤灰、矿渣微粉复合双掺时对水泥砂浆的强度以及抗模拟酸雨侵蚀性能的影响。
The above materials cover pigment, dyes, ferrous powder, cement, fly ash, dried mortar powder, antimony oxide, talc powder and calcium carbonate.
颜料、染料、铁粉、水泥、粉煤灰、干粉砂浆、氧化锑、滑石粉、碳酸钙等。
The above materials cover pigment, dyes, ferrous powder, cement, fly ash, dried mortar powder, antimony oxide, talc powder and calcium carbonate.
颜料、染料、铁粉、水泥、粉煤灰、干粉砂浆、氧化锑、滑石粉、碳酸钙等。