Fracture lines start from the outside and spread over the whole cross section, particularly starting in the fillet area and very often after a fatigue crack propagation.
断裂面从轴承部位外部开始延伸到整个截面。典型的是从圆弧部开始，常常会由于疲劳而产生的裂纹的扩展后引起的。
The primary failure model is fatigue fracture that is always resulted by the crack initiation and propagation.
疲劳断裂是气门弹簧失效的主要模式，它是疲劳裂纹萌生及其扩展的结果。
The mechanical properties of the butt welded joints have been evaluated according to the impulsive and fracture toughness as well as the rate and threshold values of fatigue crack propagation.
根据试验测定的焊缝各区冲击韧性、断裂韧性、疲劳裂纹扩展速率和疲劳裂纹扩展门槛值，对焊缝力学性能作出综合评价。
The results showed that manufacturing defects of the bolt resulted in initiation and propagation of fatigue crack, and uneven loading of the bolt speeded up failure process of fatigue fracture.
确认螺栓机加工不当引起疲劳裂纹的萌生及扩展，加之螺栓受力不均匀加速了疲劳断裂过程。
In addition, the crack propagation and fatigue damage of CSP under wind load in the case of the material which have initial crack have been analyzed using fracture mechanics method.
此外，还运用断裂力学方法分析了材料有初始裂纹的管道在风荷载作用下的裂纹扩展及疲劳损伤。
The fatigue fractography consists of several different zones, including fatigue crack initiation, slow, fast propagation and final fracture.
疲劳断口上存在典型的疲劳裂纹萌生区、缓慢扩展区、快速扩展区和最后瞬断区。
The main course of fatigue fracture is due to existence of the inclusion in the material. The inclusion induce crack initiation, the crack propagation and the axe fracture in the circle stress.
疲劳断裂的主要原因是在材料中存在的夹杂物诱发裂纹源，在循环应力的作用下裂纹扩展导致断裂。
The equiaxed structure has good tensile property, low fracture toughness and high fatigue crack propagation rate.
等轴组织具有较好的拉伸性能、低的断裂韧性和高的疲劳裂纹扩展速率；
The equiaxed structure has good tensile property, low fracture toughness and high fatigue crack propagation rate.
等轴组织具有较好的拉伸性能、低的断裂韧性和高的疲劳裂纹扩展速率；